6mm Toughened Glass by Elite Safety Glass
It is processed by heating 6mm clear float glass, 6mm low iron glass, 6mm tinted glass, 6mm patterned glass, 6mm acid etched glass, or 6mm frosted glass to 650 degrees softening point, and then quenched rapidly. It creates tension inside the glass and compression outside the glass surface.
6mm Toughened Glass Options
6mm Clear float glass, 6mm Extra Clear Glass, 6mm Patterned Glass, 6mm Mirror Glass, 6mm Silk Screen Glass, 6mm Digital Printing Glass, 6mm Sand-Blasted Glass, 6mm Acid Etched Glass, 6mm Frosted Glass.
6mm Ford Blue Glass, 6mm Diamond Blue Glass, 6mm Ocean Blue Glass. 6mm Crystal Grey Glass, 6mm Jinjing Grey Glass, 6mm Euro Grey Glass. 6mm French Green Glass, 6mm Natural Green Glass. 6mm PG10/PG20 Black Glass, etc.
Heating Time
6mm clear/low iron tempered glass in Radiant furnace: 39s/mm, total 233 seconds~243 seconds
6mm clear/low iron toughened glass in Forced Convection furnace: 28s/mm, 165 seconds~175 seconds
6mm tinted/colored tempered glass in Radiant furnace: 35s/mm, 211 seconds~221 seconds
6mm tinted/colored toughened glass in Forced Convection furnace: 28s/mm, 165 seconds~175 seconds
Quench Time
6mm toughened glass Quench Time=Glass Thickness^1.8=6mm^1.8=25s
Compression & Tension Zone
21% (1.26mm) up & down part with compression, 58% (3.48mm) middle part with tension.
Surface compression >90Mpa (over 13000Psi).
6mm Toughened Glass Standard & Certificate
North American
ASTM C1048 standard, SGCC certificate
Europe
EN12150 standard, CE certificate
Australia & New Zealand
AS/NZS2208-1996 standard, AS/NZS 2208 certificate
Features & Benefits
Flatness Quality
<0.2% local bow & <0.3% arc bow standard, with non-visual defects in the surface.
Flexibility
3~5 stable cooperative factories to guarantee lead time based on different requests.
Turnkey Solution
From smaller size glass louver to giant glass 3660mm*18000mm toughened glass.
Safety
when 6mm tempered glass panel is broken, it will break into granularities to prevent series of injuries.
Strength
6mm toughened glass is about 4~5 times stronger than 6mm annealed glass.
Stability
6mm clear and low iron toughened glass can withstand 280℃ temperature variation.
Applications
Framed Glass Balustrade
Glass Bookcase
Glass Partition
Glass Shelf
Glass Shower
Glass Splashback
Glass Table Top