10mm Toughened Glass by Elite Safety Glass
It is processed by heating 10mm clear float glass, 10mm low iron glass, or 10mm Low-e glass to 650 degrees softening point, and then quenched rapidly. It creates tension inside the glass and compression outside the glass surface.
10mm clear/low iron tempered glass in Radiant furnace: 39s/mm, total 388 seconds~398 seconds
10mm clear/low iron toughened glass in Forced Convection furnace: 28s/mm, 275 seconds~285 seconds
10mm tinted/colored tempered glass in Radiant furnace: 35s/mm, 352 seconds~362 seconds
10mm tinted/colored toughened glass in Forced Convection furnace: 28s/mm, 275 seconds~285 seconds
10mm toughened glass Quench Time=Glass Thickness^1.8=10mm^1.8=63s
Compression & Tension Zone
21% (2.10mm) up & down part with compression, 58% (5.80mm) middle part with tension.
Surface compression >90Mpa (over 13000Psi).
10mm Toughened Glass Standard & Certificate
ASTM C1048 standard, SGCC certificate
EN12150 standard, CE certificate
Australia & New Zealand
AS/NZS2208-1996 standard, AS/NZS 2208 certificate
Features & Benefits
<0.2% local bow & <0.3% arc bow standard, with non-visual defects in the surface.
3~5 stable cooperative factories to guarantee lead time based on different requests.
From smaller size glass louver to giant glass 3660mm*18000mm toughened glass.
when 10mm tempered glass is broken, it will break into granularities to prevent series of injuries.
10mm tempered glass is about 4~5 times stronger than 10mm annealed glass.
10mm toughened glass can withstand 280℃ temperature variation.
Semi-frame pool fence
Glass table top
Windows, doors, facades